温度条件对焦炭热强度的影响规律研究
Study on the Influence of Temperature Conditions on the Coke Thermal Strength
程欢,张洪波,梁英华等
点击:115次 下载:0次
作者单位:华北理工大学,河钢集团唐钢公司
中文关键字:温度条件; 焦炭; 热强度;高炉
英文关键字: temperature conditions; coke; thermal strength; blast furnace
中文摘要: 揭示温度条件对焦炭热强度的影响规律。采用自主研发的焦炭热强度检测方法,考察1050℃、1100℃、1150℃、1200℃、1250℃、1300℃ 6个温度条件下的焦炭热强度值变化。实验结果表明:不同温度条件下测得的等溶损反应后强度CSR25值与CSR指标存在显著差异,且两者之间没有明显的正相关性。反应温度T不同,焦炭的溶损反应模式不一样,导致不同焦炭的CSR25-T曲线的形状有差异。根据凹口位置,可以大致分为三类,凹口处于低温区域的I型,凹口处于中温区域的II型和凹口处于高温区域的III型。温度条件对焦炭测得的热强度值具有重要影响,国标CSR方法只检测1100℃一个温度点是不够的,应根据温度条件变化,提出更具模拟性的焦炭热强度表征指标。
英文摘要: The influence of temperature conditions on the coke thermal strength was revealed. The variation of coke thermal strength values under the six temperature conditions of 1050℃, 1100℃, 1150℃, 1200℃, 1250℃, 1300℃ was investigated by using the self-developed coke thermal strength detection method. The experimental results show that, a significant difference existed between the strength after iso-loss reaction CSR25 values measured at different temperatures and the CSR indexes, and there was no obvious positive correlation between them. When the reaction temperature T was different, the carbon solution loss reaction model was different, which led to the different shapes of CSR25-T curves of various cokes. According to the position of the notch, the CSR25-T curves can be roughly divided into three types, i.e. Type I of the notch in the low temperature region, Type II of the notch in the intermediate temperature region, and Type III of the notch in the high temperature region. The temperature conditions have important influence on the coke thermal strength. It is not enough to detect only one temperature point at 1100℃ by the Chinese national standard CSR method. A more representative characterization index of coke thermal strength should be put forward according to the variation of reaction temperature conditions.
读者评论

      读者ID: 密码:    点击此处进行授权 点击此处进行授权
我要评论:
国内统一连续出版物号:61-1134/TG |国内发行代码:52-64 |国际标准出版物号:1000-8365 |国际发行代码:M855
主管单位:西安市科学技术协会  主办单位:中国铸造协会 西安市铸造学会
开户银行:中国工商银行西安市互助路支行  帐户名:陕西铸造技术杂志社有限责任公司  帐号:3700 0235 0920 0091 309
版权所有©2019铸造技术》编辑部 陕ICP备11009796号
本系统由北京菲斯特诺科技有限公司设计开发
您是本站第10797466名访问者 网站管理